# CIF generated by HEAS from Alexandria entry agm003246744
data_agm003246744
_cell_length_a     11.08261
_cell_length_b     11.08261
_cell_length_c     11.08261
_cell_angle_alpha  117.72271
_cell_angle_beta   117.72271
_cell_angle_gamma  93.99182
_cell_volume       993.04613
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  Er1 Er 0.16996 0.66996 0.83992 1.00000
  Er2 Er 0.83004 0.33004 0.16008 1.00000
  Er3 Er 0.66996 0.83004 0.50000 1.00000
  Er4 Er 0.33004 0.16996 0.50000 1.00000
  Er5 Er 0.83097 0.69760 0.26030 1.00000
  Er6 Er 0.16903 0.30240 0.73970 1.00000
  Er7 Er 0.43729 0.57067 0.73970 1.00000
  Er8 Er 0.69760 0.43729 0.86663 1.00000
  Er9 Er 0.06271 0.80240 0.13337 1.00000
  Er10 Er 0.56271 0.42933 0.26030 1.00000
  Er11 Er 0.30240 0.56271 0.13337 1.00000
  Er12 Er 0.93729 0.19760 0.86663 1.00000
  Er13 Er 0.57067 0.83097 0.13337 1.00000
  Er14 Er 0.66903 0.92933 0.86663 1.00000
  Er15 Er 0.42933 0.16903 0.86663 1.00000
  Er16 Er 0.33097 0.07067 0.13337 1.00000
  Er17 Er 0.92933 0.06271 0.26030 1.00000
  Er18 Er 0.07067 0.93729 0.73970 1.00000
  Er19 Er 0.80240 0.66903 0.73970 1.00000
  Er20 Er 0.19760 0.33097 0.26030 1.00000
  Er21 Er 0.14755 0.64755 0.50000 1.00000
  Er22 Er 0.85245 0.35245 0.50000 1.00000
  Er23 Er 0.64755 0.14755 0.50000 1.00000
  Er24 Er 0.35245 0.85245 0.50000 1.00000
  Al1 Al 0.62031 0.12031 0.74063 1.00000
  Al2 Al 0.37969 0.87969 0.25937 1.00000
  Al3 Al 0.12031 0.37969 0.50000 1.00000
  Al4 Al 0.87969 0.62031 0.50000 1.00000
  Al5 Al 0.38188 0.88188 0.85530 1.00000
  Al6 Al 0.61812 0.11812 0.14470 1.00000
  Al7 Al 0.02658 0.52658 0.14470 1.00000
  Al8 Al 0.88188 0.02658 0.50000 1.00000
  Al9 Al 0.47342 0.61812 0.50000 1.00000
  Al10 Al 0.97342 0.47342 0.85530 1.00000
  Al11 Al 0.11812 0.97342 0.50000 1.00000
  Al12 Al 0.52658 0.38188 0.50000 1.00000
  Si1 Si 0.50000 0.50000 0.00000 1.00000
  Si2 Si 0.00000 0.00000 0.00000 1.00000
  Si3 Si 0.75000 0.75000 0.00000 1.00000
  Si4 Si 0.25000 0.25000 0.00000 1.00000