# CIF generated by HEAS from Alexandria entry agm005228701 data_agm005228701 _cell_length_a 10.23579 _cell_length_b 10.23579 _cell_length_c 23.09293 _cell_angle_alpha 90.00000 _cell_angle_beta 90.00000 _cell_angle_gamma 120.00000 _cell_volume 2095.32890 _symmetry_space_group_name_H-M 'P 1' _symmetry_Int_Tables_number 1 loop_ _symmetry_equiv_pos_as_xyz 'x, y, z' loop_ _atom_site_label _atom_site_type_symbol _atom_site_fract_x _atom_site_fract_y _atom_site_fract_z _atom_site_occupancy La1 La 0.20720 0.41439 0.71869 1.00000 La2 La 0.20720 0.79280 0.71869 1.00000 La3 La 0.79280 0.58561 0.21869 1.00000 La4 La 0.58561 0.79280 0.71869 1.00000 La5 La 0.79280 0.20720 0.21869 1.00000 La6 La 0.41439 0.20720 0.21869 1.00000 La7 La 0.79237 0.58473 0.94836 1.00000 La8 La 0.79237 0.20763 0.94836 1.00000 La9 La 0.20763 0.41527 0.44836 1.00000 La10 La 0.41527 0.20763 0.94836 1.00000 La11 La 0.20763 0.79237 0.44836 1.00000 La12 La 0.58473 0.79237 0.44836 1.00000 La13 La 0.20739 0.41479 0.99036 1.00000 La14 La 0.20739 0.79261 0.99036 1.00000 La15 La 0.79261 0.58521 0.49036 1.00000 La16 La 0.58521 0.79261 0.99036 1.00000 La17 La 0.79261 0.20739 0.49036 1.00000 La18 La 0.41479 0.20739 0.49036 1.00000 La19 La 0.87226 0.74452 0.63388 1.00000 La20 La 0.87226 0.12774 0.63388 1.00000 La21 La 0.12774 0.25548 0.13388 1.00000 La22 La 0.25548 0.12774 0.63388 1.00000 La23 La 0.12774 0.87226 0.13388 1.00000 La24 La 0.74452 0.87226 0.13388 1.00000 La25 La 0.46042 0.92083 0.85519 1.00000 La26 La 0.46042 0.53958 0.85519 1.00000 La27 La 0.53958 0.07917 0.35519 1.00000 La28 La 0.07917 0.53958 0.85519 1.00000 La29 La 0.53958 0.46042 0.35519 1.00000 La30 La 0.92083 0.46042 0.35519 1.00000 La31 La 0.00000 0.00000 0.99970 1.00000 La32 La 0.00000 0.00000 0.49970 1.00000 La33 La 0.46039 0.92078 0.58635 1.00000 La34 La 0.46039 0.53961 0.58635 1.00000 La35 La 0.53961 0.07922 0.08635 1.00000 La36 La 0.07922 0.53961 0.58635 1.00000 La37 La 0.53961 0.46039 0.08635 1.00000 La38 La 0.92078 0.46039 0.08635 1.00000 La39 La 0.79416 0.58831 0.78186 1.00000 La40 La 0.79416 0.20584 0.78186 1.00000 La41 La 0.20584 0.41169 0.28186 1.00000 La42 La 0.41169 0.20584 0.78186 1.00000 La43 La 0.20584 0.79416 0.28186 1.00000 La44 La 0.58831 0.79416 0.28186 1.00000 La45 La 0.66667 0.33333 0.64701 1.00000 La46 La 0.33333 0.66667 0.14701 1.00000 Mg1 Mg 0.00000 0.00000 0.74995 1.00000 Mg2 Mg 0.00000 0.00000 0.24995 1.00000 Mg3 Mg 0.10481 0.20962 0.86238 1.00000 Mg4 Mg 0.10481 0.89519 0.86238 1.00000 Mg5 Mg 0.89519 0.79038 0.36238 1.00000 Mg6 Mg 0.79038 0.89519 0.86238 1.00000 Mg7 Mg 0.89519 0.10481 0.36238 1.00000 Mg8 Mg 0.20962 0.10481 0.36238 1.00000 Ir1 Ir 0.51967 0.03933 0.71165 1.00000 Ir2 Ir 0.51967 0.48033 0.71165 1.00000 Ir3 Ir 0.48033 0.96067 0.21165 1.00000 Ir4 Ir 0.96067 0.48033 0.71165 1.00000 Ir5 Ir 0.48033 0.51967 0.21165 1.00000 Ir6 Ir 0.03933 0.51967 0.21165 1.00000 Ir7 Ir 0.66667 0.33333 0.86563 1.00000 Ir8 Ir 0.33333 0.66667 0.36563 1.00000 Ir9 Ir 0.14408 0.28815 0.56275 1.00000 Ir10 Ir 0.14408 0.85592 0.56275 1.00000 Ir11 Ir 0.85592 0.71185 0.06275 1.00000 Ir12 Ir 0.71185 0.85592 0.56275 1.00000 Ir13 Ir 0.85592 0.14408 0.06275 1.00000 Ir14 Ir 0.28815 0.14408 0.06275 1.00000