# CIF generated by HEAS from Alexandria entry agm005249059
data_agm005249059
_cell_length_a     10.96180
_cell_length_b     10.96180
_cell_length_c     10.96180
_cell_angle_alpha  93.99041
_cell_angle_beta   93.99041
_cell_angle_gamma  149.40889
_cell_volume       646.57906
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  Tm1 Tm 0.69356 0.50000 0.19356 1.00000
  Tm2 Tm 0.14021 0.85979 0.00000 1.00000
  Tm3 Tm 0.85979 0.14021 0.00000 1.00000
  Tm4 Tm 0.30644 0.50000 0.80644 1.00000
  Tm5 Tm 0.50000 0.30644 0.80644 1.00000
  Tm6 Tm 0.85979 0.85979 0.71958 1.00000
  Tm7 Tm 0.14021 0.14021 0.28042 1.00000
  Tm8 Tm 0.50000 0.69356 0.19356 1.00000
  Mn1 Mn 0.10020 0.60020 0.20040 1.00000
  Mn2 Mn 0.10020 0.89980 0.50000 1.00000
  Mn3 Mn 0.89980 0.39980 0.79960 1.00000
  Mn4 Mn 0.60020 0.10020 0.20040 1.00000
  Mn5 Mn 0.60020 0.39980 0.50000 1.00000
  Mn6 Mn 0.39980 0.60020 0.50000 1.00000
  Mn7 Mn 0.89980 0.10020 0.50000 1.00000
  Mn8 Mn 0.39980 0.89980 0.79960 1.00000
  Sn1 Sn 0.29622 0.70378 0.00000 1.00000
  Sn2 Sn 0.71277 0.00000 0.71277 1.00000
  Sn3 Sn 0.24944 0.24944 0.00000 1.00000
  Sn4 Sn 0.00000 0.71277 0.71277 1.00000
  Sn5 Sn 0.70378 0.29622 0.00000 1.00000
  Sn6 Sn 0.70378 0.70378 0.40756 1.00000
  Sn7 Sn 0.50000 0.90273 0.40273 1.00000
  Sn8 Sn 0.90273 0.50000 0.40273 1.00000
  Sn9 Sn 0.00000 0.28723 0.28723 1.00000
  Sn10 Sn 0.75056 0.75056 0.00000 1.00000
  Sn11 Sn 0.09727 0.50000 0.59727 1.00000
  Sn12 Sn 0.28723 0.00000 0.28723 1.00000
  Sn13 Sn 0.50000 0.09727 0.59727 1.00000
  Sn14 Sn 0.29622 0.29622 0.59244 1.00000