# CIF generated by HEAS from Alexandria entry agm005253293
data_agm005253293
_cell_length_a     3.82621
_cell_length_b     3.82621
_cell_length_c     39.15238
_cell_angle_alpha  90.00000
_cell_angle_beta   90.00000
_cell_angle_gamma  120.00000
_cell_volume       496.39407
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  Zn1 Zn 0.00000 0.00000 0.81934 1.00000
  Zn2 Zn 0.33333 0.66667 0.65456 1.00000
  Zn3 Zn 0.33333 0.66667 0.25122 1.00000
  Zn4 Zn 0.00000 0.00000 0.33187 1.00000
  Zn5 Zn 0.00000 0.00000 0.57381 1.00000
  Zn6 Zn 0.00000 0.00000 0.17059 1.00000
  Zn7 Zn 0.66667 0.33333 0.41245 1.00000
  Zn8 Zn 0.66667 0.33333 0.08994 1.00000
  Zn9 Zn 0.66667 0.33333 0.73519 1.00000
  Zn10 Zn 0.33333 0.66667 0.86824 1.00000
  Zn11 Zn 0.33333 0.66667 0.49308 1.00000
  Zn12 Zn 0.33333 0.66667 0.00887 1.00000
  S1 S 0.00000 0.00000 0.23095 1.00000
  S2 S 0.66667 0.33333 0.47286 1.00000
  S3 S 0.33333 0.66667 0.71493 1.00000
  S4 S 0.00000 0.00000 0.63431 1.00000
  S5 S 0.00000 0.00000 0.98995 1.00000
  S6 S 0.66667 0.33333 0.15044 1.00000
  S7 S 0.33333 0.66667 0.31168 1.00000
  S8 S 0.33333 0.66667 0.92450 1.00000
  S9 S 0.33333 0.66667 0.07002 1.00000
  S10 S 0.00000 0.00000 0.39224 1.00000
  S11 S 0.33333 0.66667 0.55347 1.00000
  S12 S 0.66667 0.33333 0.79549 1.00000