# CIF generated by HEAS from Alexandria entry agm005271990
data_agm005271990
_cell_length_a     7.57207
_cell_length_b     7.57207
_cell_length_c     13.37072
_cell_angle_alpha  90.00000
_cell_angle_beta   90.00000
_cell_angle_gamma  120.00000
_cell_volume       663.91870
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  Sm1 Sm 0.33333 0.66667 0.75000 1.00000
  Sm2 Sm 0.66667 0.33333 0.25000 1.00000
  Co1 Co 0.00000 0.00000 0.00000 1.00000
  Co2 Co 0.00000 0.00000 0.50000 1.00000
  C1 C 0.76788 0.88396 0.91899 1.00000
  C2 C 0.23212 0.11604 0.08101 1.00000
  C3 C 0.11608 0.23212 0.91899 1.00000
  C4 C 0.23212 0.11604 0.41899 1.00000
  C5 C 0.88392 0.76788 0.08101 1.00000
  C6 C 0.76788 0.88396 0.58101 1.00000
  C7 C 0.11604 0.88392 0.91899 1.00000
  C8 C 0.88392 0.76788 0.41899 1.00000
  C9 C 0.88396 0.11608 0.08101 1.00000
  C10 C 0.11608 0.23212 0.58101 1.00000
  C11 C 0.88396 0.11608 0.41899 1.00000
  C12 C 0.11604 0.88392 0.58101 1.00000
  N1 N 0.62271 0.81136 0.86796 1.00000
  N2 N 0.37729 0.18864 0.13204 1.00000
  N3 N 0.18865 0.37729 0.86796 1.00000
  N4 N 0.37729 0.18864 0.36796 1.00000
  N5 N 0.81135 0.62271 0.13204 1.00000
  N6 N 0.62271 0.81136 0.63204 1.00000
  N7 N 0.18864 0.81135 0.86796 1.00000
  N8 N 0.81135 0.62271 0.36796 1.00000
  N9 N 0.81136 0.18865 0.13204 1.00000
  N10 N 0.18865 0.37729 0.63204 1.00000
  N11 N 0.81136 0.18865 0.36796 1.00000
  N12 N 0.18864 0.81135 0.63204 1.00000
  O1 O 0.66667 0.33333 0.83879 1.00000
  O2 O 0.33333 0.66667 0.16121 1.00000
  O3 O 0.33333 0.66667 0.33879 1.00000
  O4 O 0.66667 0.33333 0.66121 1.00000
  O5 O 0.93177 0.46608 0.75000 1.00000
  O6 O 0.06823 0.53392 0.25000 1.00000
  O7 O 0.53432 0.06823 0.75000 1.00000
  O8 O 0.46568 0.93177 0.25000 1.00000
  O9 O 0.53392 0.46568 0.75000 1.00000
  O10 O 0.46608 0.53432 0.25000 1.00000