# CIF generated by HEAS from Alexandria entry agm005772202
data_agm005772202
_cell_length_a     6.67990
_cell_length_b     6.67990
_cell_length_c     24.72711
_cell_angle_alpha  89.99855
_cell_angle_beta   89.99855
_cell_angle_gamma  115.91269
_cell_volume       992.42078
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  Nd1 Nd 0.50000 0.00000 0.99961 1.00000
  Nd2 Nd 1.00000 0.50000 0.00039 1.00000
  Y1 Y 0.50000 0.50000 0.79895 1.00000
  Y2 Y 0.00000 0.00000 0.79895 1.00000
  Y3 Y 0.75067 0.74932 0.92087 1.00000
  Y4 Y 0.25037 0.75037 0.86883 1.00000
  Y5 Y 0.00000 0.00000 0.32643 1.00000
  Y6 Y 0.24963 0.74963 0.13117 1.00000
  Y7 Y 0.76056 0.26056 0.58773 1.00000
  Y8 Y 0.50000 0.50000 0.32643 1.00000
  Y9 Y 0.24932 0.25067 0.92087 1.00000
  Y10 Y 0.74933 0.75068 0.07913 1.00000
  Y11 Y 0.26414 0.23587 0.56102 1.00000
  Y12 Y 0.73944 0.23944 0.41227 1.00000
  Y13 Y 1.00000 1.00000 0.67357 1.00000
  Y14 Y 0.23586 0.26413 0.43898 1.00000
  Y15 Y 0.25068 0.24933 0.07913 1.00000
  Y16 Y 0.76413 0.73586 0.43898 1.00000
  Y17 Y 0.73587 0.76414 0.56102 1.00000
  Y18 Y 1.00000 1.00000 0.20105 1.00000
  Y19 Y 0.23944 0.73944 0.58773 1.00000
  Y20 Y 0.50000 0.50000 0.67357 1.00000
  Y21 Y 0.74964 0.24964 0.86883 1.00000
  Y22 Y 0.50000 0.50000 0.20105 1.00000
  Y23 Y 0.26056 0.76056 0.41227 1.00000
  Y24 Y 0.75036 0.25036 0.13117 1.00000
  Tm1 Tm 0.50000 0.00000 0.26657 1.00000
  Tm2 Tm 0.00000 0.50000 0.26927 1.00000
  Tm3 Tm 1.00000 0.50000 0.73343 1.00000
  Tm4 Tm 0.50000 1.00000 0.73073 1.00000