# CIF generated by HEAS from Alexandria entry agm006089367
data_agm006089367
_cell_length_a     8.53799
_cell_length_b     8.53799
_cell_length_c     8.53799
_cell_angle_alpha  60.00000
_cell_angle_beta   60.00001
_cell_angle_gamma  60.00000
_cell_volume       440.10057
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  Li1 Li 0.64032 0.11989 0.11989 1.00000
  Li2 Li 0.35968 0.88011 0.88011 1.00000
  Li3 Li 0.11989 0.11989 0.64032 1.00000
  Li4 Li 0.11989 0.11989 0.11989 1.00000
  Li5 Li 0.88011 0.88011 0.35968 1.00000
  Li6 Li 0.88011 0.88011 0.88011 1.00000
  Li7 Li 0.11989 0.64032 0.11989 1.00000
  Li8 Li 0.88011 0.35968 0.88011 1.00000
  Li9 Li 0.50000 0.50000 0.00000 1.00000
  Li10 Li 0.00000 0.00000 0.50000 1.00000
  Li11 Li 0.50000 0.00000 0.00000 1.00000
  Li12 Li 0.00000 0.50000 0.50000 1.00000
  Li13 Li 0.50000 0.00000 0.50000 1.00000
  Li14 Li 0.00000 0.50000 0.00000 1.00000
  Li15 Li 0.88978 0.37007 0.37007 1.00000
  Li16 Li 0.11022 0.62993 0.62993 1.00000
  Li17 Li 0.37007 0.37007 0.88978 1.00000
  Li18 Li 0.37007 0.37007 0.37007 1.00000
  Li19 Li 0.62993 0.62993 0.11022 1.00000
  Li20 Li 0.62993 0.62993 0.62993 1.00000
  Li21 Li 0.37007 0.88978 0.37007 1.00000
  Li22 Li 0.62993 0.11022 0.62993 1.00000
  Li23 Li 0.00000 0.00000 0.00000 1.00000
  Ge1 Ge 0.50000 0.50000 0.50000 1.00000
  Rh1 Rh 0.72681 0.72681 0.27319 1.00000
  Rh2 Rh 0.27319 0.27319 0.72681 1.00000
  Rh3 Rh 0.72681 0.27319 0.27319 1.00000
  Rh4 Rh 0.27319 0.72681 0.72681 1.00000
  Rh5 Rh 0.72681 0.27319 0.72681 1.00000
  Rh6 Rh 0.27319 0.72681 0.27319 1.00000