# CIF generated by HEAS from Alexandria entry agm006211069
data_agm006211069
_cell_length_a     8.32136
_cell_length_b     8.32136
_cell_length_c     10.12139
_cell_angle_alpha  90.00000
_cell_angle_beta   90.00000
_cell_angle_gamma  120.00000
_cell_volume       606.95901
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  Tc1 Tc 0.00000 0.00000 0.11239 1.00000
  Tc2 Tc 0.00000 0.00000 0.88761 1.00000
  Tc3 Tc 0.00000 0.00000 0.61239 1.00000
  Tc4 Tc 0.00000 0.00000 0.38761 1.00000
  Tc5 Tc 0.66667 0.33333 0.85296 1.00000
  Tc6 Tc 0.33333 0.66667 0.14704 1.00000
  Tc7 Tc 0.33333 0.66667 0.35296 1.00000
  Tc8 Tc 0.66667 0.33333 0.64704 1.00000
  Se1 Se 0.66667 0.33333 0.10876 1.00000
  Se2 Se 0.33333 0.66667 0.89124 1.00000
  Se3 Se 0.33333 0.66667 0.60876 1.00000
  Se4 Se 0.66667 0.33333 0.39124 1.00000
  Se5 Se 0.00000 0.50000 0.00000 1.00000
  Se6 Se 0.50000 0.50000 0.00000 1.00000
  Se7 Se 0.50000 0.00000 0.00000 1.00000
  Se8 Se 0.00000 0.50000 0.50000 1.00000
  Se9 Se 0.50000 0.50000 0.50000 1.00000
  Se10 Se 0.50000 0.00000 0.50000 1.00000
  Se11 Se 0.27674 0.13837 0.25000 1.00000
  Se12 Se 0.86163 0.13837 0.25000 1.00000
  Se13 Se 0.86163 0.72326 0.25000 1.00000
  Se14 Se 0.72326 0.86163 0.75000 1.00000
  Se15 Se 0.13837 0.86163 0.75000 1.00000
  Se16 Se 0.13837 0.27674 0.75000 1.00000