# CIF generated by HEAS from Alexandria entry agm006267828
data_agm006267828
_cell_length_a     7.06114
_cell_length_b     8.01214
_cell_length_c     14.08710
_cell_angle_alpha  94.92492
_cell_angle_beta   90.76114
_cell_angle_gamma  102.49535
_cell_volume       774.80914
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  Na1 Na 0.23612 0.55448 0.16941 1.00000
  Na2 Na 0.24894 0.55286 0.67154 1.00000
  Na3 Na 0.74795 0.44895 0.32803 1.00000
  Na4 Na 0.74526 0.44622 0.82561 1.00000
  Ca1 Ca 0.60117 0.84831 0.07236 1.00000
  Ca2 Ca 0.58981 0.85289 0.57231 1.00000
  Ca3 Ca 0.40499 0.14781 0.42623 1.00000
  Ca4 Ca 0.40500 0.14640 0.93073 1.00000
  Ca5 Ca 0.08154 0.84889 0.57003 1.00000
  Ca6 Ca 0.91402 0.15117 0.42967 1.00000
  Ca7 Ca 0.91911 0.15049 0.93247 1.00000
  Si1 Si 0.96341 0.20223 0.17324 1.00000
  Si2 Si 0.95043 0.21247 0.67409 1.00000
  Si3 Si 0.04556 0.79094 0.31891 1.00000
  Si4 Si 0.04484 0.78542 0.83135 1.00000
  Si5 Si 0.40739 0.21980 0.16752 1.00000
  Si6 Si 0.39968 0.21848 0.66846 1.00000
  Si7 Si 0.59555 0.78153 0.33023 1.00000
  Si8 Si 0.59610 0.78299 0.83532 1.00000
  Si9 Si 0.74707 0.45007 0.07121 1.00000
  Si10 Si 0.73384 0.45128 0.57253 1.00000
  Si11 Si 0.26174 0.55131 0.42426 1.00000
  Si12 Si 0.25764 0.55414 0.93222 1.00000
  Ni1 Ni 0.09664 0.85485 0.07040 1.00000
  H1 H 0.65156 0.16332 0.26473 1.00000
  H2 H 0.64089 0.16273 0.76721 1.00000
  H3 H 0.35119 0.83671 0.22846 1.00000
  H4 H 0.34955 0.83579 0.73785 1.00000
  O1 O 0.81359 0.65609 0.06457 1.00000
  O2 O 0.78663 0.65524 0.56401 1.00000
  O3 O 0.20725 0.34770 0.43449 1.00000
  O4 O 0.21202 0.35099 0.94440 1.00000
  O5 O 0.27780 0.68387 0.02977 1.00000
  O6 O 0.28850 0.67065 0.52513 1.00000
  O7 O 0.70410 0.33079 0.47245 1.00000
  O8 O 0.70891 0.33251 0.97008 1.00000
  O9 O 0.19972 0.26710 0.19633 1.00000
  O10 O 0.18912 0.26325 0.69460 1.00000
  O11 O 0.80598 0.73775 0.30230 1.00000
  O12 O 0.80667 0.73788 0.80928 1.00000
  O13 O 0.54105 0.40197 0.13266 1.00000
  O14 O 0.53091 0.40188 0.63595 1.00000
  O15 O 0.46906 0.59815 0.36463 1.00000
  O16 O 0.46799 0.60399 0.87435 1.00000
  O17 O 0.91289 0.38037 0.13413 1.00000
  O18 O 0.90678 0.39627 0.63962 1.00000
  O19 O 0.09534 0.60800 0.35332 1.00000
  O20 O 0.08922 0.59814 0.85864 1.00000
  O21 O 0.84925 0.16787 0.27059 1.00000
  O22 O 0.84358 0.17378 0.77308 1.00000
  O23 O 0.14756 0.82864 0.21786 1.00000
  O24 O 0.15297 0.83250 0.73305 1.00000
  O25 O 0.38426 0.06011 0.08639 1.00000
  O26 O 0.38482 0.06358 0.58561 1.00000
  O27 O 0.61044 0.93641 0.41312 1.00000
  O28 O 0.61406 0.94133 0.91642 1.00000
  O29 O 0.91714 0.04290 0.09001 1.00000
  O30 O 0.89279 0.05915 0.58860 1.00000
  O31 O 0.10556 0.94155 0.40590 1.00000
  O32 O 0.10343 0.93129 0.92110 1.00000
  O33 O 0.50739 0.18886 0.26914 1.00000
  O34 O 0.49614 0.18544 0.77070 1.00000
  O35 O 0.49513 0.81203 0.22838 1.00000
  O36 O 0.49498 0.80943 0.73296 1.00000