# CIF generated by HEAS from Alexandria entry agm008201637
data_agm008201637
_cell_length_a     6.62629
_cell_length_b     7.59187
_cell_length_c     16.24757
_cell_angle_alpha  103.37179
_cell_angle_beta   93.75388
_cell_angle_gamma  90.03859
_cell_volume       793.37984
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  V1 V 0.87872 0.68949 0.88255 1.00000
  V2 V 0.87936 0.16930 0.88740 1.00000
  V3 V 0.49632 0.97647 0.49642 1.00000
  V4 V 0.15094 0.77731 0.09944 1.00000
  V5 V 0.50345 0.48182 0.49483 1.00000
  V6 V 0.15772 0.28021 0.09489 1.00000
  Bi1 Bi 0.22386 0.58813 0.68504 1.00000
  Bi2 Bi 0.69600 0.83756 0.67178 1.00000
  Bi3 Bi 0.70238 0.35296 0.71296 1.00000
  Bi4 Bi 0.86115 0.38917 0.27069 1.00000
  Bi5 Bi 0.32766 0.63947 0.27937 1.00000
  Bi6 Bi 0.86123 0.89039 0.27181 1.00000
  Bi7 Bi 0.22104 0.10228 0.68317 1.00000
  Bi8 Bi 0.27956 0.44680 0.89518 1.00000
  Bi9 Bi 0.96934 0.25141 0.49845 1.00000
  Bi10 Bi 0.62603 0.04592 0.09271 1.00000
  Bi11 Bi 0.04915 0.74516 0.49411 1.00000
  Bi12 Bi 0.68311 0.53775 0.08077 1.00000
  Bi13 Bi 0.33559 0.16044 0.31369 1.00000
  Bi14 Bi 0.37708 0.94241 0.88080 1.00000
  O1 O 0.94542 0.43885 0.85772 1.00000
  O2 O 0.80575 0.09740 0.77481 1.00000
  O3 O 0.18186 0.90319 0.22766 1.00000
  O4 O 0.80285 0.68451 0.77470 1.00000
  O5 O 0.18298 0.33505 0.22640 1.00000
  O6 O 0.85546 0.28479 0.12639 1.00000
  O7 O 0.65222 0.67485 0.92509 1.00000
  O8 O 0.65460 0.25286 0.92658 1.00000
  O9 O 0.18154 0.14591 0.84594 1.00000
  O10 O 0.05495 0.29477 0.99241 1.00000
  O11 O 0.52826 0.24620 0.47700 1.00000
  O12 O 0.37254 0.38309 0.76439 1.00000
  O13 O 0.20236 0.05192 0.52337 1.00000
  O14 O 0.88693 0.95657 0.91258 1.00000
  O15 O 0.20377 0.48043 0.52327 1.00000
  O16 O 0.02764 0.66862 0.33203 1.00000
  O17 O 0.99750 0.32324 0.64607 1.00000
  O18 O 0.19271 0.05101 0.08374 1.00000
  O19 O 0.41717 0.87488 0.74798 1.00000
  O20 O 0.42503 0.48689 0.38556 1.00000
  O21 O 0.61174 0.11706 0.22585 1.00000
  O22 O 0.42982 0.90643 0.38490 1.00000
  O23 O 0.10877 0.57637 0.13354 1.00000
  O24 O 0.01552 0.17944 0.35472 1.00000
  O25 O 0.68157 0.61064 0.21732 1.00000
  O26 O 0.41845 0.34308 0.08961 1.00000
  O27 O 0.85244 0.85268 0.12755 1.00000
  O28 O 0.43298 0.77174 0.52640 1.00000
  O29 O 0.18542 0.70562 0.84616 1.00000
  O30 O 0.41856 0.75937 0.08981 1.00000
  O31 O 0.53494 0.53094 0.62566 1.00000
  O32 O 0.53795 0.10431 0.62710 1.00000
  O33 O 0.76410 0.54648 0.49736 1.00000
  O34 O 0.03839 0.81866 0.63421 1.00000
  O35 O 0.76169 0.95571 0.49660 1.00000
  O36 O 0.05396 0.70701 0.99383 1.00000