# CIF generated by HEAS from Alexandria entry agm010282953
data_agm010282953
_cell_length_a     10.41956
_cell_length_b     5.81639
_cell_length_c     11.18943
_cell_angle_alpha  90.00000
_cell_angle_beta   90.00021
_cell_angle_gamma  90.00000
_cell_volume       678.12703
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  Al1 Al 0.50023 0.75030 0.50016 1.00000
  Al2 Al 0.99997 0.24996 0.99992 1.00000
  Al3 Al 0.50023 0.24970 0.50016 1.00000
  Al4 Al 0.99997 0.75004 0.99992 1.00000
  Al5 Al 0.72683 0.00000 0.94699 1.00000
  Al6 Al 0.77300 0.00000 0.44836 1.00000
  Al7 Al 0.27319 0.50000 0.05246 1.00000
  Al8 Al 0.22682 0.50000 0.55194 1.00000
  Al9 Al 0.00004 0.75003 0.49987 1.00000
  Al10 Al 0.50005 0.24985 0.00017 1.00000
  Al11 Al 0.00004 0.24997 0.49987 1.00000
  Al12 Al 0.50005 0.75015 0.00017 1.00000
  Zn1 Zn 0.90913 0.00000 0.22258 1.00000
  Zn2 Zn 0.40923 0.50000 0.27788 1.00000
  Zn3 Zn 0.09056 0.50000 0.77742 1.00000
  Co1 Co 0.59005 0.00000 0.72316 1.00000
  Si1 Si 0.93447 0.00000 0.76274 1.00000
  Si2 Si 0.56591 0.00000 0.26315 1.00000
  Si3 Si 0.06560 0.50000 0.23691 1.00000
  Si4 Si 0.43387 0.50000 0.73705 1.00000
  B1 B 0.75121 0.50000 0.49974 1.00000
  B2 B 0.74892 0.50000 0.99899 1.00000
  B3 B 0.24890 0.00000 0.50038 1.00000
  B4 B 0.25111 0.00000 0.00088 1.00000
  O1 O 0.04630 0.50000 0.59710 1.00000
  O2 O 0.45401 0.50000 0.09738 1.00000
  O3 O 0.95374 0.00000 0.40276 1.00000
  O4 O 0.54603 0.00000 0.90272 1.00000
  O5 O 0.68069 0.70428 0.99925 1.00000
  O6 O 0.81942 0.29570 0.50007 1.00000
  O7 O 0.31937 0.20426 0.00056 1.00000
  O8 O 0.18071 0.79564 0.49981 1.00000
  O9 O 0.31937 0.79574 0.00056 1.00000
  O10 O 0.18071 0.20436 0.49981 1.00000
  O11 O 0.68069 0.29572 0.99925 1.00000
  O12 O 0.81942 0.70430 0.50007 1.00000
  O13 O 0.77561 0.00000 0.78873 1.00000
  O14 O 0.72451 0.00000 0.29018 1.00000
  O15 O 0.22436 0.50000 0.21036 1.00000
  O16 O 0.27540 0.50000 0.71004 1.00000
  O17 O 0.61748 0.00000 0.51995 1.00000
  O18 O 0.88232 0.00000 0.01877 1.00000
  O19 O 0.38255 0.50000 0.48079 1.00000
  O20 O 0.11762 0.50000 0.98087 1.00000
  O21 O 0.97342 0.00000 0.62043 1.00000
  O22 O 0.52749 0.00000 0.12068 1.00000
  O23 O 0.02699 0.50000 0.37932 1.00000
  O24 O 0.47251 0.50000 0.87942 1.00000
  O25 O 0.62137 0.50000 0.49644 1.00000
  O26 O 0.87873 0.50000 0.99582 1.00000
  O27 O 0.37869 0.00000 0.50411 1.00000
  O28 O 0.12129 0.00000 0.00396 1.00000
  O29 O 0.49311 0.72740 0.67024 1.00000
  O30 O 0.00657 0.27283 0.17009 1.00000
  O31 O 0.50687 0.22711 0.32997 1.00000
  O32 O 0.99327 0.77286 0.82971 1.00000
  O33 O 0.50687 0.77289 0.32997 1.00000
  O34 O 0.99327 0.22714 0.82971 1.00000
  O35 O 0.49311 0.27260 0.67024 1.00000
  O36 O 0.00657 0.72717 0.17009 1.00000