# CIF generated by HEAS from Alexandria entry agm010946907
data_agm010946907
_cell_length_a     5.54541
_cell_length_b     5.52569
_cell_length_c     25.92508
_cell_angle_alpha  89.99942
_cell_angle_beta   90.26997
_cell_angle_gamma  89.99942
_cell_volume       794.39372
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  Ho1 Ho 0.50689 0.52993 0.99858 1.00000
  Ho2 Ho 0.00209 0.46991 0.49891 1.00000
  Ho3 Ho 0.99811 0.97046 0.00111 1.00000
  Ho4 Ho 0.49334 0.02936 0.50143 1.00000
  Zr1 Zr 0.49859 0.01223 0.08336 1.00000
  Zr2 Zr 0.49242 0.49328 0.58419 1.00000
  Zr3 Zr 0.50772 0.99386 0.91581 1.00000
  Zr4 Zr 0.50164 0.51171 0.41666 1.00000
  Ta1 Ta 0.99461 0.98513 0.58181 1.00000
  Ta2 Ta 0.00558 0.48571 0.91820 1.00000
  Ta3 Ta 0.00425 0.00825 0.41802 1.00000
  Ta4 Ta 0.99599 0.50879 0.08199 1.00000
  Bi1 Bi 0.47110 0.57900 0.20080 1.00000
  Bi2 Bi 0.96742 0.45305 0.70192 1.00000
  Bi3 Bi 0.96253 0.56291 0.30034 1.00000
  Bi4 Bi 0.03710 0.06295 0.19963 1.00000
  Bi5 Bi 0.53093 0.92915 0.69896 1.00000
  Bi6 Bi 0.46852 0.42920 0.80101 1.00000
  Bi7 Bi 0.52851 0.07892 0.29914 1.00000
  Bi8 Bi 0.03199 0.95306 0.79804 1.00000
  O1 O 0.68381 0.34069 0.07666 1.00000
  O2 O 0.26264 0.29204 0.25025 1.00000
  O3 O 0.08915 0.04151 0.50053 1.00000
  O4 O 0.73707 0.79205 0.24972 1.00000
  O5 O 0.21887 0.76707 0.94126 1.00000
  O6 O 0.16979 0.32424 0.41270 1.00000
  O7 O 0.78132 0.26648 0.55876 1.00000
  O8 O 0.23289 0.79084 0.25086 1.00000
  O9 O 0.70588 0.78330 0.55487 1.00000
  O10 O 0.91015 0.00404 0.65155 1.00000
  O11 O 0.07590 0.45938 0.15165 1.00000
  O12 O 0.16072 0.67129 0.57569 1.00000
  O13 O 0.40409 0.45005 0.49945 1.00000
  O14 O 0.83942 0.17192 0.92434 1.00000
  O15 O 0.80221 0.72614 0.44419 1.00000
  O16 O 0.76680 0.29078 0.24910 1.00000
  O17 O 0.41282 0.96363 0.15751 1.00000
  O18 O 0.31643 0.84014 0.42336 1.00000
  O19 O 0.30286 0.15896 0.58769 1.00000
  O20 O 0.57056 0.55083 0.65836 1.00000
  O21 O 0.25389 0.71382 0.74894 1.00000
  O22 O 0.74559 0.21368 0.75103 1.00000
  O23 O 0.83053 0.82483 0.08731 1.00000
  O24 O 0.92422 0.95892 0.34837 1.00000
  O25 O 0.08981 0.50453 0.84845 1.00000
  O26 O 0.59612 0.95061 0.00057 1.00000
  O27 O 0.58722 0.46342 0.34249 1.00000
  O28 O 0.27508 0.71872 0.05722 1.00000
  O29 O 0.42927 0.05116 0.84166 1.00000
  O30 O 0.69739 0.65962 0.91234 1.00000
  O31 O 0.91109 0.54208 0.99949 1.00000
  O32 O 0.29436 0.28395 0.94513 1.00000
  O33 O 0.72517 0.21820 0.44279 1.00000
  O34 O 0.19807 0.22671 0.05581 1.00000
  O35 O 0.23339 0.21877 0.74916 1.00000
  O36 O 0.76610 0.71873 0.75084 1.00000