# CIF generated by HEAS from Alexandria entry agm011978982
data_agm011978982
_cell_length_a     9.01345
_cell_length_b     9.01345
_cell_length_c     5.72572
_cell_angle_alpha  90.00000
_cell_angle_beta   90.00000
_cell_angle_gamma  120.00000
_cell_volume       402.84972
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  Al1 Al 0.46052 0.00416 0.75000 1.00000
  Al2 Al 0.45636 0.99584 0.25000 1.00000
  Al3 Al 0.53948 0.54364 0.25000 1.00000
  Al4 Al 0.54364 0.53948 0.75000 1.00000
  Al5 Al 0.99584 0.45636 0.75000 1.00000
  Al6 Al 0.00416 0.46052 0.25000 1.00000
  B1 B 0.80725 0.00000 0.50000 1.00000
  B2 B 0.80725 0.00000 0.00000 1.00000
  B3 B 0.00000 0.80725 0.50000 1.00000
  B4 B 0.19275 0.19275 0.50000 1.00000
  B5 B 0.19275 0.19275 0.00000 1.00000
  B6 B 0.00000 0.80725 0.00000 1.00000
  B7 B 0.66667 0.33333 0.25000 1.00000
  B8 B 0.33333 0.66667 0.75000 1.00000
  Ir1 Ir 0.81012 0.53588 0.50512 1.00000
  Ir2 Ir 0.53588 0.81012 0.49488 1.00000
  Ir3 Ir 0.99554 0.17951 0.75000 1.00000
  Ir4 Ir 0.27424 0.46412 0.49488 1.00000
  Ir5 Ir 0.00446 0.18398 0.25000 1.00000
  Ir6 Ir 0.72576 0.18988 0.50512 1.00000
  Ir7 Ir 0.81602 0.82049 0.25000 1.00000
  Ir8 Ir 0.18988 0.72576 0.49488 1.00000
  Ir9 Ir 0.46412 0.27424 0.50512 1.00000
  Ir10 Ir 0.81012 0.53588 0.99488 1.00000
  Ir11 Ir 0.46412 0.27424 0.99488 1.00000
  Ir12 Ir 0.18398 0.00446 0.75000 1.00000
  Ir13 Ir 0.17951 0.99554 0.25000 1.00000
  Ir14 Ir 0.18988 0.72576 0.00512 1.00000
  Ir15 Ir 0.82049 0.81602 0.75000 1.00000
  Ir16 Ir 0.72576 0.18988 0.99488 1.00000
  Ir17 Ir 0.27424 0.46412 0.00512 1.00000
  Ir18 Ir 0.53588 0.81012 0.00512 1.00000