# CIF generated by HEAS from Alexandria entry agm017184813
data_agm017184813
_cell_length_a     12.16428
_cell_length_b     12.16428
_cell_length_c     3.73517
_cell_angle_alpha  90.00000
_cell_angle_beta   90.00000
_cell_angle_gamma  120.00000
_cell_volume       478.64503
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  Tm1 Tm 0.81378 0.00000 0.50000 1.00000
  Tm2 Tm 0.00000 0.81378 0.50000 1.00000
  Tm3 Tm 0.18622 0.18622 0.50000 1.00000
  Tm4 Tm 0.33333 0.66667 0.00000 1.00000
  Tm5 Tm 0.66667 0.33333 0.00000 1.00000
  Ti1 Ti 0.43949 0.00000 0.00000 1.00000
  Ti2 Ti 0.00000 0.43949 0.00000 1.00000
  Ti3 Ti 0.56051 0.56051 0.00000 1.00000
  Ni1 Ni 0.27721 0.00000 0.50000 1.00000
  Ni2 Ni 0.00000 0.27721 0.50000 1.00000
  Ni3 Ni 0.72279 0.72279 0.50000 1.00000
  Ni4 Ni 0.62227 0.80636 0.00000 1.00000
  Ni5 Ni 0.19364 0.81592 0.00000 1.00000
  Ni6 Ni 0.18408 0.37773 0.00000 1.00000
  Ni7 Ni 0.37773 0.18408 0.00000 1.00000
  Ni8 Ni 0.80636 0.62227 0.00000 1.00000
  Ni9 Ni 0.81592 0.19364 0.00000 1.00000
  Ni10 Ni 0.51494 0.87517 0.50000 1.00000
  Ni11 Ni 0.12483 0.63978 0.50000 1.00000
  Ni12 Ni 0.36022 0.48506 0.50000 1.00000
  Ni13 Ni 0.48506 0.36022 0.50000 1.00000
  Ni14 Ni 0.87517 0.51494 0.50000 1.00000
  Ni15 Ni 0.63978 0.12483 0.50000 1.00000
  Ni16 Ni 0.00000 0.00000 0.00000 1.00000
  P1 P 0.17764 0.00000 0.00000 1.00000
  P2 P 0.00000 0.17764 0.00000 1.00000
  P3 P 0.82236 0.82236 0.00000 1.00000
  P4 P 0.52212 0.68878 0.50000 1.00000
  P5 P 0.31122 0.83334 0.50000 1.00000
  P6 P 0.16666 0.47788 0.50000 1.00000
  P7 P 0.47788 0.16666 0.50000 1.00000
  P8 P 0.68878 0.52212 0.50000 1.00000
  P9 P 0.83334 0.31122 0.50000 1.00000
  P10 P 0.63837 0.00000 0.00000 1.00000
  P11 P 0.00000 0.63837 0.00000 1.00000
  P12 P 0.36163 0.36163 0.00000 1.00000