# CIF generated by HEAS from Alexandria entry agm017394697
data_agm017394697
_cell_length_a     7.39108
_cell_length_b     11.86257
_cell_length_c     12.66635
_cell_angle_alpha  90.00000
_cell_angle_beta   90.00000
_cell_angle_gamma  90.00000
_cell_volume       1110.55059
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  La1 La 0.25218 0.25073 0.33304 1.00000
  La2 La 0.25218 0.74927 0.66696 1.00000
  La3 La 0.74782 0.75073 0.16696 1.00000
  La4 La 0.74782 0.24927 0.83304 1.00000
  La5 La 0.74782 0.74927 0.66696 1.00000
  La6 La 0.74782 0.25073 0.33304 1.00000
  La7 La 0.25218 0.24927 0.83304 1.00000
  La8 La 0.25218 0.75073 0.16696 1.00000
  La9 La 0.50000 0.00191 0.24757 1.00000
  La10 La 0.50000 0.99809 0.75243 1.00000
  La11 La 0.50000 0.50191 0.25243 1.00000
  La12 La 0.50000 0.49809 0.74757 1.00000
  La13 La 0.00000 0.00140 0.24801 1.00000
  La14 La 0.00000 0.99860 0.75199 1.00000
  La15 La 0.00000 0.50140 0.25199 1.00000
  La16 La 0.00000 0.49860 0.74801 1.00000
  La17 La 0.25335 0.00000 0.50000 1.00000
  La18 La 0.74665 0.50000 0.00000 1.00000
  La19 La 0.74665 0.00000 0.50000 1.00000
  La20 La 0.25335 0.50000 0.00000 1.00000
  Y1 Y 0.00000 0.25209 0.58252 1.00000
  Y2 Y 0.00000 0.74791 0.41748 1.00000
  Y3 Y 0.00000 0.75209 0.91748 1.00000
  Y4 Y 0.00000 0.24791 0.08252 1.00000
  Y5 Y 0.25150 0.50000 0.50000 1.00000
  Y6 Y 0.74850 0.00000 0.00000 1.00000
  Y7 Y 0.74850 0.50000 0.50000 1.00000
  Y8 Y 0.25150 0.00000 0.00000 1.00000
  Tm1 Tm 0.50000 0.24801 0.08302 1.00000
  Tm2 Tm 0.50000 0.75199 0.91698 1.00000
  Tm3 Tm 0.50000 0.74801 0.41698 1.00000
  Tm4 Tm 0.50000 0.25199 0.58302 1.00000