# CIF generated by HEAS from Alexandria entry agm020279423
data_agm020279423
_cell_length_a     20.00703
_cell_length_b     10.15787
_cell_length_c     10.22717
_cell_angle_alpha  72.83011
_cell_angle_beta   90.00000
_cell_angle_gamma  90.00000
_cell_volume       1985.82722
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  Cs1 Cs 0.31092 0.59294 0.09195 1.00000
  Cs2 Cs 0.81092 0.90706 0.90805 1.00000
  Cs3 Cs 0.68908 0.40706 0.90805 1.00000
  Cs4 Cs 0.18908 0.09294 0.09195 1.00000
  La1 La 0.45238 0.73346 0.48652 1.00000
  La2 La 0.63927 0.90098 0.52089 1.00000
  La3 La 0.54762 0.26654 0.51348 1.00000
  La4 La 0.98438 0.59614 0.20120 1.00000
  La5 La 0.51562 0.09614 0.20120 1.00000
  La6 La 0.86073 0.40098 0.52089 1.00000
  La7 La 0.04762 0.23346 0.48652 1.00000
  La8 La 0.13927 0.59902 0.47911 1.00000
  La9 La 0.95238 0.76654 0.51348 1.00000
  La10 La 0.01562 0.40386 0.79880 1.00000
  La11 La 0.48438 0.90386 0.79880 1.00000
  La12 La 0.36073 0.09902 0.47911 1.00000
  Pd1 Pd 0.50000 0.00000 0.50000 1.00000
  Pd2 Pd 0.00000 0.50000 0.50000 1.00000
  I1 I 0.06379 0.09741 0.81141 1.00000
  I2 I 0.20687 0.31551 0.42341 1.00000
  I3 I 0.17381 0.48739 0.80322 1.00000
  I4 I 0.70687 0.18449 0.57659 1.00000
  I5 I 0.43621 0.59741 0.81141 1.00000
  I6 I 0.53044 0.19565 0.85077 1.00000
  I7 I 0.46956 0.80435 0.14923 1.00000
  I8 I 0.09932 0.91561 0.47823 1.00000
  I9 I 0.56379 0.40259 0.18859 1.00000
  I10 I 0.86297 0.28459 0.85471 1.00000
  I11 I 0.36297 0.21541 0.14529 1.00000
  I12 I 0.67381 0.01261 0.19678 1.00000
  I13 I 0.59932 0.58439 0.52177 1.00000
  I14 I 0.03044 0.30435 0.14923 1.00000
  I15 I 0.79313 0.68449 0.57659 1.00000
  I16 I 0.29313 0.81551 0.42341 1.00000
  I17 I 0.90068 0.08439 0.52177 1.00000
  I18 I 0.40068 0.41561 0.47823 1.00000
  I19 I 0.93621 0.90259 0.18859 1.00000
  I20 I 0.63703 0.78459 0.85471 1.00000
  I21 I 0.13703 0.71541 0.14529 1.00000
  I22 I 0.82619 0.51262 0.19678 1.00000
  I23 I 0.96956 0.69565 0.85077 1.00000
  I24 I 0.32619 0.98738 0.80322 1.00000