# CIF generated by HEAS from Alexandria entry agm021479928
data_agm021479928
_cell_length_a     6.31620
_cell_length_b     2.91594
_cell_length_c     22.72318
_cell_angle_alpha  90.00000
_cell_angle_beta   95.23053
_cell_angle_gamma  90.00000
_cell_volume       416.76609
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  Na1 Na 0.30416 0.50000 0.60266 1.00000
  Na2 Na 0.09796 0.00000 0.70001 1.00000
  Na3 Na 0.89773 0.50000 0.80019 1.00000
  Na4 Na 0.69935 0.00000 0.90019 1.00000
  Na5 Na 0.50000 0.50000 0.00000 1.00000
  Na6 Na 0.30065 0.00000 0.09981 1.00000
  Na7 Na 0.90204 0.00000 0.29999 1.00000
  Na8 Na 0.10227 0.50000 0.19981 1.00000
  Na9 Na 0.69584 0.50000 0.39734 1.00000
  Na10 Na 0.50000 0.00000 0.50000 1.00000
  Ni1 Ni 0.78783 0.50000 0.60256 1.00000
  Ni2 Ni 0.59608 0.00000 0.69981 1.00000
  Ni3 Ni 0.39848 0.50000 0.80034 1.00000
  Ni4 Ni 0.19925 0.00000 0.90015 1.00000
  Ni5 Ni 0.80075 0.00000 0.09985 1.00000
  Ni6 Ni 0.00000 0.50000 0.00000 1.00000
  Ni7 Ni 0.60152 0.50000 0.19966 1.00000
  Ni8 Ni 0.40392 0.00000 0.30019 1.00000
  Ni9 Ni 0.21217 0.50000 0.39744 1.00000
  Ru1 Ru 0.00000 0.00000 0.50000 1.00000
  O1 O 0.78001 0.50000 0.50121 1.00000
  O2 O 0.57973 0.00000 0.60471 1.00000
  O3 O 0.80177 0.50000 0.69664 1.00000
  O4 O 0.00889 0.00000 0.58863 1.00000
  O5 O 0.60062 0.00000 0.79752 1.00000
  O6 O 0.39400 0.50000 0.70491 1.00000
  O7 O 0.99754 0.50000 0.90318 1.00000
  O8 O 0.19634 0.00000 0.80323 1.00000
  O9 O 0.40087 0.50000 0.89706 1.00000
  O10 O 0.79825 0.00000 0.00311 1.00000
  O11 O 0.20175 0.00000 0.99689 1.00000
  O12 O 0.80366 0.00000 0.19677 1.00000
  O13 O 0.59913 0.50000 0.10294 1.00000
  O14 O 0.00246 0.50000 0.09682 1.00000
  O15 O 0.39938 0.00000 0.20248 1.00000
  O16 O 0.60600 0.50000 0.29509 1.00000
  O17 O 0.99111 0.00000 0.41137 1.00000
  O18 O 0.19823 0.50000 0.30336 1.00000
  O19 O 0.42027 0.00000 0.39529 1.00000
  O20 O 0.21999 0.50000 0.49879 1.00000