# CIF generated by HEAS from Alexandria entry agm032150124
data_agm032150124
_cell_length_a     7.35716
_cell_length_b     7.35716
_cell_length_c     12.33896
_cell_angle_alpha  90.00000
_cell_angle_beta   90.00000
_cell_angle_gamma  120.00000
_cell_volume       578.40197
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  K1 K 0.66667 0.33333 0.53244 1.00000
  K2 K 0.33333 0.66667 0.03244 1.00000
  K3 K 0.66667 0.33333 0.94396 1.00000
  K4 K 0.33333 0.66667 0.44396 1.00000
  W1 W 0.66129 0.83065 0.76375 1.00000
  W2 W 0.16935 0.33871 0.76375 1.00000
  W3 W 0.33871 0.16935 0.26375 1.00000
  W4 W 0.16935 0.83065 0.76375 1.00000
  W5 W 0.83065 0.66129 0.26375 1.00000
  W6 W 0.83065 0.16935 0.26375 1.00000
  Se1 Se 0.00000 0.00000 0.99439 1.00000
  Se2 Se 0.00000 0.00000 0.49439 1.00000
  O1 O 0.75132 0.87566 0.93474 1.00000
  O2 O 0.12434 0.24868 0.93474 1.00000
  O3 O 0.24868 0.12434 0.43474 1.00000
  O4 O 0.12434 0.87566 0.93474 1.00000
  O5 O 0.87566 0.75132 0.43474 1.00000
  O6 O 0.87566 0.12434 0.43474 1.00000
  O7 O 0.45649 0.54351 0.80968 1.00000
  O8 O 0.08701 0.54351 0.80968 1.00000
  O9 O 0.54351 0.45649 0.30968 1.00000
  O10 O 0.45649 0.91299 0.80968 1.00000
  O11 O 0.91299 0.45649 0.30968 1.00000
  O12 O 0.54351 0.08701 0.30968 1.00000
  O13 O 0.59667 0.79834 0.62425 1.00000
  O14 O 0.20166 0.40333 0.62425 1.00000
  O15 O 0.40333 0.20166 0.12425 1.00000
  O16 O 0.20166 0.79834 0.62425 1.00000
  O17 O 0.79834 0.59667 0.12425 1.00000
  O18 O 0.79834 0.20166 0.12425 1.00000
  O19 O 0.87517 0.12483 0.75194 1.00000
  O20 O 0.24966 0.12483 0.75194 1.00000
  O21 O 0.12483 0.87517 0.25194 1.00000
  O22 O 0.87517 0.75034 0.75194 1.00000
  O23 O 0.75034 0.87517 0.25194 1.00000
  O24 O 0.12483 0.24966 0.25194 1.00000