# CIF generated by HEAS from Alexandria entry agm034268276
data_agm034268276
_cell_length_a     6.80154
_cell_length_b     4.38634
_cell_length_c     23.42135
_cell_angle_alpha  90.00000
_cell_angle_beta   90.02199
_cell_angle_gamma  90.00000
_cell_volume       698.75005
_symmetry_space_group_name_H-M 'P 1'
_symmetry_Int_Tables_number 1
loop_
_symmetry_equiv_pos_as_xyz
  'x, y, z'
loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
  Ho1 Ho 0.53269 0.00000 0.94023 1.00000
  Ho2 Ho 0.53443 0.00000 0.60772 1.00000
  Ho3 Ho 0.53446 0.00000 0.27408 1.00000
  Ho4 Ho 0.03271 0.00000 0.89222 1.00000
  Ho5 Ho 0.03156 0.00000 0.56063 1.00000
  Ho6 Ho 0.03096 0.00000 0.22679 1.00000
  Ho7 Ho 0.47091 0.50000 0.72735 1.00000
  Ho8 Ho 0.47476 0.50000 0.39325 1.00000
  Ho9 Ho 0.47375 0.50000 0.05973 1.00000
  Ho10 Ho 0.97100 0.50000 0.77280 1.00000
  Ho11 Ho 0.96706 0.50000 0.43916 1.00000
  Ho12 Ho 0.96584 0.50000 0.10558 1.00000
  Al1 Al 0.63901 0.00000 0.81174 1.00000
  Al2 Al 0.64424 0.00000 0.47900 1.00000
  Al3 Al 0.64291 0.00000 0.14568 1.00000
  Al4 Al 0.13978 0.00000 0.68832 1.00000
  Al5 Al 0.13905 0.00000 0.35394 1.00000
  Al6 Al 0.13719 0.00000 0.02046 1.00000
  Al7 Al 0.35546 0.50000 0.85323 1.00000
  Al8 Al 0.35940 0.50000 0.52025 1.00000
  Al9 Al 0.35788 0.50000 0.18701 1.00000
  Al10 Al 0.85632 0.50000 0.97990 1.00000
  Al11 Al 0.85675 0.50000 0.64708 1.00000
  Al12 Al 0.85700 0.50000 0.31354 1.00000
  Ir1 Ir 0.76748 0.00000 0.70609 1.00000
  Ir2 Ir 0.76743 0.00000 0.37315 1.00000
  Ir3 Ir 0.76569 0.00000 0.04001 1.00000
  Ir4 Ir 0.26686 0.00000 0.79384 1.00000
  Pt1 Pt 0.26984 0.00000 0.46022 1.00000
  Pt2 Pt 0.26889 0.00000 0.12701 1.00000
  Pt3 Pt 0.23052 0.50000 0.96027 1.00000
  Pt4 Pt 0.23191 0.50000 0.62599 1.00000
  Pt5 Pt 0.23168 0.50000 0.29328 1.00000
  Pt6 Pt 0.73062 0.50000 0.87353 1.00000
  Pt7 Pt 0.73244 0.50000 0.54008 1.00000
  Pt8 Pt 0.73154 0.50000 0.20683 1.00000