SiO2
弹性数据 ELAMP-ID: mp-558733 · 空间群: C2/c (#15)
基础信息
化学式
SiO2
MP-ID
mp-558733
元素数
2
位点数
18
密度
4.0767
g/cm³
体积
146.84
ų
晶胞参数 a
6.8550
Å
晶胞参数 b
6.8550
Å
晶胞参数 c
4.6432
Å
α 角
79.68
°
β 角
79.68
°
γ 角
43.31
°
空间群
C2/c
点群
2/m
晶体系统
Monoclinic
Bravais 格子
mC
稳定性
No
堆积分数
-
X 射线衍射
衍射图谱
横轴为 2θ (°)，纵轴为相对强度，Cu Kα ， λ=1.5418 Å
衍射峰（Top 24）
| 2θ | d (Å) | I | hkl |
|---|---|---|---|
| 26.27 | 3.3927 | 13.4 | (1,0,1) |
| 27.73 | 3.2167 | 100.0 | (2,1,0) |
| 28.28 | 3.1557 | 17.0 | (1,0,-1) |
| 31.57 | 2.8339 | 69.4 | (2,1,1) |
| 36.51 | 2.4609 | 26.4 | (2,1,-1) |
| 39.40 | 2.2869 | 4.1 | (1,1,2) |
| 39.56 | 2.2781 | 2.3 | (0,0,2) |
| 40.80 | 2.2114 | 8.3 | (1,-1,1) |
| 44.47 | 2.0375 | 6.8 | (2,2,2) |
| 44.73 | 2.0261 | 15.6 | (2,0,-1) |
| 44.90 | 2.0188 | 28.2 | (1,1,-2) |
| 48.13 | 1.8907 | 40.6 | (3,1,1) |
| 52.06 | 1.7568 | 9.4 | (3,2,2) |
| 52.57 | 1.7409 | 10.0 | (2,1,-2) |
| 52.91 | 1.7306 | 10.6 | (3,1,-1) |
| 53.57 | 1.7106 | 10.2 | (3,3,2) |
| 54.06 | 1.6963 | 1.2 | (2,0,2) |
| 54.20 | 1.6923 | 6.9 | (2,2,-2) |
| 54.55 | 1.6824 | 2.7 | (4,3,1) |
| 57.28 | 1.6084 | 2.1 | (4,2,0) |
| 57.89 | 1.5928 | 33.0 | (4,2,1) |
| 59.10 | 1.5631 | 18.3 | (3,0,0) |
| 59.40 | 1.5560 | 1.2 | (2,-1,-1) |
| 61.29 | 1.5125 | 2.9 | (3,0,1) |
能量属性
形成能/原子
-3.00914
eV/atom
能量/原子
-8.11622
eV/atom
凸包距离
0.2637
eV/atom
未修正能量
-7.6582
eV/atom
体积/原子
8.16
ų
c/a 比
0.6774
电子属性
金属性
非金属
带隙
5.270
eV
直接带隙
No
CBM
N/A
eV
磁性属性
磁性
No
总磁矩
0.0000
μB
磁有序
NM
磁性位点数
0
磁化强度/体积
0.000000
μB/ų
弹性属性
KVRH
263.994
GPa
GVRH
193.946
GPa
杨氏模量 E
467.382
GPa
泊松比 ν
0.205
Pugh 比 K/G
1.361
维氏硬度估算
27.384
GPa
韧性
Ductile
各向异性
0.025
拉梅 λ
134.697
GPa
特征分析
元素组成（原子分数）
组成信息
主元 / 基质元素
O · 0.667
元素家族
Metalloid-Nonmetal
溶质分数
0.333
间隙分数
0.333
弹性模量对比 (GPa)
弹性特征
弹性各向异性 AU
0.0250
均匀泊松比 ν
0.2050
Debye 温度
1,451.4
K
声速
7,618.7
m/s
均匀度
0.2050
关联任务
引用参考
Materials Project 官方页面
https://materialsproject.org/materials/mp-558733
参考引用
The crystal structure and related material properties of SiO2 were obtained from the Materials Project database (MP-ID: mp-558733, database version v2026.04.13).
文献引用
Horton, M.K., Huck, P., Yang, R.X. et al. Accelerated data-driven materials science with the Materials Project. Nat. Mater. 24, 1522–1532 (2025). https://doi.org/10.1038/s41563-025-02272-0
晶体结构 3D 渲染
加载 3D 结构...
样式: Ball & Stick
|
拖拽旋转 · 滚轮缩放 · 右键平移
原始 CIF 数据
# generated using pymatgen
data_SiO2
_symmetry_space_group_name_H-M 'P 1'
_cell_length_a 6.85498438
_cell_length_b 6.85498438
_cell_length_c 4.64319546
_cell_angle_alpha 79.67772194
_cell_angle_beta 79.67772194
_cell_angle_gamma 43.30501584
_symmetry_Int_Tables_number 1
_chemical_formula_structural SiO2
_chemical_formula_sum 'Si6 O12'
_cell_volume 146.84351579
_cell_formula_units_Z 6
loop_
_symmetry_equiv_pos_site_id
_symmetry_equiv_pos_as_xyz
1 'x, y, z'
loop_
_atom_site_type_symbol
_atom_site_label
_atom_site_symmetry_multiplicity
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
Si Si0 1 0.69172200 0.98119700 0.32968800 1.0
Si Si1 1 0.30827800 0.01880300 0.67031200 1.0
Si Si2 1 0.35780900 0.64219100 0.25000000 1.0
Si Si3 1 0.98119700 0.69172200 0.82968800 1.0
Si Si4 1 0.64219100 0.35780900 0.75000000 1.0
Si Si5 1 0.01880300 0.30827800 0.17031200 1.0
O O6 1 0.96325100 0.21874800 0.53957600 1.0
O O7 1 0.30241100 0.54857100 0.96123200 1.0
O O8 1 0.21874800 0.96325100 0.03957600 1.0
O O9 1 0.69758900 0.45142900 0.03876800 1.0
O O10 1 0.86025900 0.65657200 0.18065900 1.0
O O11 1 0.34342800 0.13974100 0.31934100 1.0
O O12 1 0.13974100 0.34342800 0.81934100 1.0
O O13 1 0.03674900 0.78125200 0.46042400 1.0
O O14 1 0.65657200 0.86025900 0.68065900 1.0
O O15 1 0.54857100 0.30241100 0.46123200 1.0
O O16 1 0.78125200 0.03674900 0.96042400 1.0
O O17 1 0.45142900 0.69758900 0.53876800 1.0