基础信息
化学式
Zn22CuIr2
MP-ID
mp-3270475
元素数
3
位点数
25
密度
8.7522
g/cm³
体积
358.01
ų
晶胞参数 a
7.6582
Å
晶胞参数 b
7.6582
Å
晶胞参数 c
7.6505
Å
α 角
72.38
°
β 角
72.38
°
γ 角
58.28
°
空间群
Cm
点群
m
晶体系统
Monoclinic
Bravais 格子
mC
稳定性
Yes
堆积分数
-
X 射线衍射
衍射图谱
横轴为 2θ (°)，纵轴为相对强度，Cu Kα ， λ=1.5418 Å
衍射峰（Top 24）
| 2θ | d (Å) | I | hkl |
|---|---|---|---|
| 13.81 | 6.4113 | 9.6 | (1,0,0) |
| 14.11 | 6.2746 | 6.0 | (1,1,0) |
| 15.20 | 5.8295 | 16.2 | (1,1,1) |
| 16.83 | 5.2668 | 24.3 | (1,0,1) |
| 20.14 | 4.4091 | 33.7 | (1,0,-1) |
| 21.81 | 4.0755 | 4.6 | (1,1,-1) |
| 23.86 | 3.7290 | 10.8 | (1,-1,0) |
| 24.40 | 3.6484 | 14.3 | (1,2,0) |
| 24.40 | 3.6484 | 14.3 | (2,1,0) |
| 24.81 | 3.5883 | 11.1 | (0,0,2) |
| 26.23 | 3.3981 | 5.4 | (1,0,2) |
| 26.78 | 3.3290 | 3.3 | (2,2,1) |
| 27.83 | 3.2056 | 1.3 | (0,2,0) |
| 27.83 | 3.2056 | 1.3 | (2,0,0) |
| 28.41 | 3.1413 | 11.1 | (2,0,1) |
| 29.16 | 3.0625 | 8.9 | (2,1,2) |
| 30.66 | 2.9157 | 1.1 | (2,1,-1) |
| 30.67 | 2.9148 | 3.4 | (2,2,2) |
| 32.76 | 2.7334 | 1.4 | (1,1,-2) |
| 34.69 | 2.5856 | 1.6 | (1,-1,2) |
| 34.96 | 2.5667 | 1.4 | (2,2,-1) |
| 35.22 | 2.5484 | 2.4 | (1,1,3) |
| 35.65 | 2.5184 | 2.8 | (3,2,1) |
| 36.17 | 2.4834 | 1.6 | (1,3,1) |
能量属性
形成能/原子
-0.14146
eV/atom
能量/原子
-12.60541
eV/atom
凸包距离
0.0000
eV/atom
未修正能量
-12.6054
eV/atom
体积/原子
14.32
ų
c/a 比
0.9990
电子属性
金属性
金属
带隙
0
eV
直接带隙
No
CBM
N/A
eV
磁性属性
磁性
No
总磁矩
0.0031
μB
磁有序
NM
磁性位点数
0
磁化强度/体积
0.000010
μB/ų
弹性属性
弹性数据暂不开放
特征分析
元素组成（原子分数）
组成信息
主元 / 基质元素
Zn · 0.880
元素家族
3d-TM
溶质分数
0.120
间隙分数
0.000
综合指标雷达（归一化）
元素类别占比
混合熵 ΔS/R
0.4433
高熵判据（>1.0 视为高熵）
混合熵 ΔS
3.6857
J/mol·K
Ω 参数
0.8163
Ω > 1.1 利于固溶体形成
原子尺寸错配 δr
0.989%
δr < 6.6% 利于单相固溶
电负性差 Δχ
0.1542
越小混合越稳定
VEC
11.720
价电子浓度，影响相稳定性
混合焓 ΔH_mix
-3.987
kJ/mol 且负值为放热混合
熵归一化
0.4035
固溶体倾向
1
相趋势
SS
关联任务
关联的计算任务 ID（1 个）
引用参考
Materials Project 官方页面
https://materialsproject.org/materials/mp-3270475
参考引用
The crystal structure and related material properties of Zn22CuIr2 were obtained from the Materials Project database (MP-ID: mp-3270475, database version v2026.04.13).
文献引用
Horton, M.K., Huck, P., Yang, R.X. et al. Accelerated data-driven materials science with the Materials Project. Nat. Mater. 24, 1522–1532 (2025). https://doi.org/10.1038/s41563-025-02272-0
晶体结构 3D 渲染
加载 3D 结构...
样式: Ball & Stick
|
拖拽旋转 · 滚轮缩放 · 右键平移
原始 CIF 数据
# generated using pymatgen
data_Zn22CuIr2
_symmetry_space_group_name_H-M 'P 1'
_cell_length_a 7.65819297
_cell_length_b 7.65819428
_cell_length_c 7.65050071
_cell_angle_alpha 72.38265060
_cell_angle_beta 72.38264708
_cell_angle_gamma 58.27843643
_symmetry_Int_Tables_number 1
_chemical_formula_structural Zn22CuIr2
_chemical_formula_sum 'Zn22 Cu1 Ir2'
_cell_volume 358.01263592
_cell_formula_units_Z 1
loop_
_symmetry_equiv_pos_site_id
_symmetry_equiv_pos_as_xyz
1 'x, y, z'
loop_
_atom_site_type_symbol
_atom_site_label
_atom_site_symmetry_multiplicity
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
Zn Zn0 1 0.34613699 0.73610206 0.31106120 1.0
Zn Zn1 1 0.65631602 0.26043907 0.68527248 1.0
Zn Zn2 1 0.26043907 0.65631602 0.68527248 1.0
Zn Zn3 1 0.73610206 0.34613699 0.31106120 1.0
Zn Zn4 1 0.68057628 0.32167461 0.99852957 1.0
Zn Zn5 1 0.32167461 0.68057628 0.99852957 1.0
Zn Zn6 1 0.82906752 0.82906752 0.78759913 1.0
Zn Zn7 1 0.17018341 0.17018341 0.21866336 1.0
Zn Zn8 1 0.97599377 0.97599377 0.17126977 1.0
Zn Zn9 1 0.02576671 0.02576671 0.82672823 1.0
Zn Zn10 1 0.35811297 0.35811297 0.27589553 1.0
Zn Zn11 1 0.64675710 0.64675710 0.72693433 1.0
Zn Zn12 1 0.68517015 0.68517015 0.37867547 1.0
Zn Zn13 1 0.31153667 0.31153667 0.62171232 1.0
Zn Zn14 1 0.65965760 0.02305119 0.45712670 1.0
Zn Zn15 1 0.34504748 0.97210895 0.54154695 1.0
Zn Zn16 1 0.97210895 0.34504748 0.54154695 1.0
Zn Zn17 1 0.02305119 0.65965760 0.45712670 1.0
Zn Zn18 1 0.62265106 0.99400741 0.10428085 1.0
Zn Zn19 1 0.38528936 0.99569072 0.89666672 1.0
Zn Zn20 1 0.99569072 0.38528936 0.89666672 1.0
Zn Zn21 1 0.99400741 0.62265106 0.10428085 1.0
Cu Cu22 1 0.65691582 0.65691582 0.05680712 1.0
Ir Ir23 1 0.34146085 0.34146085 0.94585653 1.0
Ir Ir24 1 0.00028424 0.00028424 0.50089024 1.0