基础信息
化学式
CaAc11Ga12
MP-ID
mp-3281426
元素数
3
位点数
24
密度
7.6000
g/cm³
体积
737.14
ų
晶胞参数 a
4.3756
Å
晶胞参数 b
14.2349
Å
晶胞参数 c
11.8347
Å
α 角
89.99
°
β 角
90.00
°
γ 角
90.00
°
空间群
Pmm2
点群
mm2
晶体系统
Orthorhombic
Bravais 格子
oP
稳定性
Yes
堆积分数
-
X 射线衍射
衍射图谱
横轴为 2θ (°)，纵轴为相对强度，Cu Kα ， λ=1.5418 Å
衍射峰（Top 24）
| 2θ | d (Å) | I | hkl |
|---|---|---|---|
| 6.21 | 14.2349 | 6.6 | (0,1,0) |
| 7.47 | 11.8347 | 4.9 | (0,0,1) |
| 9.72 | 9.1010 | 3.0 | (0,1,1) |
| 9.72 | 9.0998 | 3.0 | (0,1,-1) |
| 12.44 | 7.1175 | 1.8 | (0,2,0) |
| 14.52 | 6.0998 | 1.5 | (0,2,1) |
| 14.52 | 6.0990 | 1.4 | (0,2,-1) |
| 14.97 | 5.9173 | 2.5 | (0,0,2) |
| 16.22 | 5.4643 | 1.2 | (0,1,2) |
| 16.22 | 5.4638 | 1.2 | (0,1,-2) |
| 20.16 | 4.4044 | 13.6 | (0,3,1) |
| 20.16 | 4.4040 | 13.5 | (0,3,-1) |
| 21.24 | 4.1825 | 1.4 | (1,1,0) |
| 21.65 | 4.1041 | 1.3 | (1,0,1) |
| 22.55 | 3.9435 | 1.2 | (1,1,1) |
| 22.55 | 3.9434 | 1.2 | (1,1,-1) |
| 25.05 | 3.5554 | 1.0 | (1,2,1) |
| 25.05 | 3.5553 | 1.0 | (1,2,-1) |
| 25.32 | 3.5182 | 84.8 | (1,0,2) |
| 28.76 | 3.1041 | 99.7 | (1,3,1) |
| 28.76 | 3.1040 | 100.0 | (1,3,-1) |
| 29.44 | 3.0337 | 55.7 | (0,3,3) |
| 29.45 | 3.0333 | 55.7 | (0,3,-3) |
| 30.21 | 2.9587 | 48.3 | (0,0,4) |
能量属性
形成能/原子
-0.60055
eV/atom
能量/原子
-38.07404
eV/atom
凸包距离
0.0000
eV/atom
未修正能量
-38.0740
eV/atom
体积/原子
30.71
ų
c/a 比
2.7047
电子属性
金属性
金属
带隙
0
eV
直接带隙
No
CBM
N/A
eV
磁性属性
磁性
No
总磁矩
0.0615
μB
磁有序
NM
磁性位点数
0
磁化强度/体积
0.000080
μB/ų
弹性属性
弹性数据暂不开放
特征分析
元素组成（原子分数）
组成信息
主元 / 基质元素
Ga · 0.500
元素家族
PostTransition-Noble
溶质分数
0.500
间隙分数
0.000
综合指标雷达（归一化）
元素类别占比
混合熵 ΔS/R
0.8366
高熵判据（>1.0 视为高熵）
混合熵 ΔS
6.9552
J/mol·K
Ω 参数
2.6160
Ω > 1.1 利于固溶体形成
原子尺寸错配 δr
18.225%
δr < 6.6% 利于单相固溶
电负性差 Δχ
0.3597
越小混合越稳定
VEC
2.500
价电子浓度，影响相稳定性
混合焓 ΔH_mix
-2.138
kJ/mol 且负值为放热混合
熵归一化
0.7615
固溶体倾向
0
相趋势
IM
关联任务
关联的计算任务 ID（1 个）
引用参考
Materials Project 官方页面
https://materialsproject.org/materials/mp-3281426
参考引用
The crystal structure and related material properties of CaAc11Ga12 were obtained from the Materials Project database (MP-ID: mp-3281426, database version v2026.04.13).
文献引用
Horton, M.K., Huck, P., Yang, R.X. et al. Accelerated data-driven materials science with the Materials Project. Nat. Mater. 24, 1522–1532 (2025). https://doi.org/10.1038/s41563-025-02272-0
晶体结构 3D 渲染
加载 3D 结构...
样式: Ball & Stick
|
拖拽旋转 · 滚轮缩放 · 右键平移
原始 CIF 数据
# generated using pymatgen
data_CaAc11Ga12
_symmetry_space_group_name_H-M 'P 1'
_cell_length_a 4.37560228
_cell_length_b 14.23492963
_cell_length_c 11.83468296
_cell_angle_alpha 89.99220978
_cell_angle_beta 90.00000000
_cell_angle_gamma 90.00000000
_symmetry_Int_Tables_number 1
_chemical_formula_structural CaAc11Ga12
_chemical_formula_sum 'Ca1 Ac11 Ga12'
_cell_volume 737.13967766
_cell_formula_units_Z 1
loop_
_symmetry_equiv_pos_site_id
_symmetry_equiv_pos_as_xyz
1 'x, y, z'
loop_
_atom_site_type_symbol
_atom_site_label
_atom_site_symmetry_multiplicity
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
Ca Ca0 1 0.75000000 0.50020979 0.63139108 1.0
Ac Ac1 1 0.25000000 0.66306151 0.85779665 1.0
Ac Ac2 1 0.25000000 0.83125784 0.36006528 1.0
Ac Ac3 1 0.75000000 0.33426346 0.13965204 1.0
Ac Ac4 1 0.75000000 0.16661022 0.64119600 1.0
Ac Ac5 1 0.25000000 0.33635516 0.85891940 1.0
Ac Ac6 1 0.25000000 0.16921880 0.36096673 1.0
Ac Ac7 1 0.75000000 0.66592924 0.13858816 1.0
Ac Ac8 1 0.75000000 0.83326289 0.64036309 1.0
Ac Ac9 1 0.25000000 0.00026041 0.86129426 1.0
Ac Ac10 1 0.25000000 0.49987749 0.36318272 1.0
Ac Ac11 1 0.75000000 0.99952295 0.14033659 1.0
Ga Ga12 1 0.25000000 0.33512078 0.56906580 1.0
Ga Ga13 1 0.25000000 0.16739896 0.06551989 1.0
Ga Ga14 1 0.75000000 0.66461517 0.43785968 1.0
Ga Ga15 1 0.75000000 0.83217750 0.93358687 1.0
Ga Ga16 1 0.25000000 0.66518272 0.56741648 1.0
Ga Ga17 1 0.25000000 0.83224129 0.06376177 1.0
Ga Ga18 1 0.75000000 0.33547125 0.43966297 1.0
Ga Ga19 1 0.75000000 0.16778807 0.93540427 1.0
Ga Ga20 1 0.25000000 0.00000321 0.56383909 1.0
Ga Ga21 1 0.25000000 0.50000341 0.06442920 1.0
Ga Ga22 1 0.75000000 0.00032355 0.43341227 1.0
Ga Ga23 1 0.75000000 0.49984933 0.93228970 1.0