基础信息
化学式
Lu3AlPt8
MP-ID
mp-3290078
元素数
3
位点数
24
密度
17.6107
g/cm³
体积
398.39
ų
晶胞参数 a
17.0152
Å
晶胞参数 b
4.1065
Å
晶胞参数 c
5.7016
Å
α 角
90.00
°
β 角
90.00
°
γ 角
90.00
°
空间群
Pmma
点群
mmm
晶体系统
Orthorhombic
Bravais 格子
oP
稳定性
Yes
堆积分数
-
X 射线衍射
衍射图谱
横轴为 2θ (°)，纵轴为相对强度，Cu Kα ， λ=1.5418 Å
衍射峰（Top 24）
| 2θ | d (Å) | I | hkl |
|---|---|---|---|
| 10.40 | 8.5076 | 4.1 | (2,0,0) |
| 15.54 | 5.7016 | 2.5 | (0,0,1) |
| 18.74 | 4.7363 | 2.1 | (2,0,1) |
| 20.88 | 4.2538 | 1.4 | (4,0,0) |
| 24.06 | 3.6983 | 2.0 | (2,1,0) |
| 26.14 | 3.4095 | 1.6 | (4,0,1) |
| 26.75 | 3.3322 | 1.8 | (0,1,1) |
| 28.77 | 3.1027 | 3.3 | (2,1,1) |
| 30.25 | 2.9545 | 2.9 | (4,1,0) |
| 30.59 | 2.9221 | 1.0 | (5,0,1) |
| 34.18 | 2.6232 | 3.9 | (4,1,1) |
| 35.23 | 2.5472 | 1.8 | (3,0,2) |
| 37.79 | 2.3809 | 1.3 | (5,1,1) |
| 38.44 | 2.3418 | 70.7 | (0,1,2) |
| 38.58 | 2.3335 | 100.0 | (6,1,0) |
| 38.82 | 2.3200 | 31.9 | (1,1,2) |
| 40.34 | 2.2360 | 1.4 | (7,0,1) |
| 41.31 | 2.1853 | 14.9 | (5,0,2) |
| 41.73 | 2.1646 | 3.1 | (3,1,2) |
| 41.83 | 2.1596 | 1.0 | (6,1,1) |
| 44.11 | 2.0533 | 36.1 | (0,2,0) |
| 45.09 | 2.0105 | 43.4 | (6,0,2) |
| 46.23 | 1.9638 | 1.3 | (7,1,1) |
| 49.26 | 1.8497 | 6.7 | (7,0,2) |
能量属性
形成能/原子
-1.26611
eV/atom
能量/原子
-45.67223
eV/atom
凸包距离
0.0000
eV/atom
未修正能量
-45.6722
eV/atom
体积/原子
16.60
ų
c/a 比
0.3351
电子属性
金属性
金属
带隙
0
eV
直接带隙
No
CBM
N/A
eV
磁性属性
磁性
No
总磁矩
0.0007
μB
磁有序
NM
磁性位点数
0
磁化强度/体积
0.000000
μB/ų
弹性属性
弹性数据暂不开放
特征分析
元素组成（原子分数）
组成信息
主元 / 基质元素
Pt · 0.667
元素家族
5d-TM
溶质分数
0.333
间隙分数
0.000
综合指标雷达（归一化）
元素类别占比
混合熵 ΔS/R
0.8240
高熵判据（>1.0 视为高熵）
混合熵 ΔS
6.8504
J/mol·K
Ω 参数
1.3151
Ω > 1.1 利于固溶体形成
原子尺寸错配 δr
10.405%
δr < 6.6% 利于单相固溶
电负性差 Δχ
0.4443
越小混合越稳定
VEC
7.417
价电子浓度，影响相稳定性
混合焓 ΔH_mix
-10.000
kJ/mol 且负值为放热混合
熵归一化
0.7500
固溶体倾向
0
相趋势
IM
关联任务
关联的计算任务 ID（1 个）
引用参考
Materials Project 官方页面
https://materialsproject.org/materials/mp-3290078
参考引用
The crystal structure and related material properties of Lu3AlPt8 were obtained from the Materials Project database (MP-ID: mp-3290078, database version v2026.04.13).
文献引用
Horton, M.K., Huck, P., Yang, R.X. et al. Accelerated data-driven materials science with the Materials Project. Nat. Mater. 24, 1522–1532 (2025). https://doi.org/10.1038/s41563-025-02272-0
晶体结构 3D 渲染
加载 3D 结构...
样式: Ball & Stick
|
拖拽旋转 · 滚轮缩放 · 右键平移
原始 CIF 数据
# generated using pymatgen
data_Lu3AlPt8
_symmetry_space_group_name_H-M 'P 1'
_cell_length_a 17.01517263
_cell_length_b 4.10653828
_cell_length_c 5.70160665
_cell_angle_alpha 90.00000000
_cell_angle_beta 90.00000000
_cell_angle_gamma 90.00000000
_symmetry_Int_Tables_number 1
_chemical_formula_structural Lu3AlPt8
_chemical_formula_sum 'Lu6 Al2 Pt16'
_cell_volume 398.39097077
_cell_formula_units_Z 2
loop_
_symmetry_equiv_pos_site_id
_symmetry_equiv_pos_as_xyz
1 'x, y, z'
loop_
_atom_site_type_symbol
_atom_site_label
_atom_site_symmetry_multiplicity
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
Lu Lu0 1 0.09012952 0.00000000 0.30603955 1.0
Lu Lu1 1 0.40987048 0.00000000 0.30603955 1.0
Lu Lu2 1 0.59012952 0.00000000 0.69396045 1.0
Lu Lu3 1 0.90986948 0.00000000 0.69396045 1.0
Lu Lu4 1 0.25000000 0.00000000 0.79864251 1.0
Lu Lu5 1 0.75000000 0.00000000 0.20135849 1.0
Al Al6 1 0.00000000 0.49999900 0.00000000 1.0
Al Al7 1 0.50000000 0.49999900 0.00000000 1.0
Pt Pt8 1 0.25000000 0.00000000 0.29375425 1.0
Pt Pt9 1 0.75000000 0.00000000 0.70624675 1.0
Pt Pt10 1 0.16619645 0.49999900 0.55295019 1.0
Pt Pt11 1 0.33380355 0.49999900 0.55295019 1.0
Pt Pt12 1 0.66619545 0.49999900 0.44704881 1.0
Pt Pt13 1 0.83380455 0.49999900 0.44704881 1.0
Pt Pt14 1 0.16206936 0.49999900 0.04836767 1.0
Pt Pt15 1 0.33793164 0.49999900 0.04836767 1.0
Pt Pt16 1 0.66206936 0.49999900 0.95163133 1.0
Pt Pt17 1 0.83793164 0.49999900 0.95163133 1.0
Pt Pt18 1 0.00000000 0.49999900 0.49999900 1.0
Pt Pt19 1 0.50000000 0.49999900 0.49999900 1.0
Pt Pt20 1 0.07279159 0.00000000 0.80456800 1.0
Pt Pt21 1 0.42720841 0.00000000 0.80456800 1.0
Pt Pt22 1 0.57279059 0.00000000 0.19543200 1.0
Pt Pt23 1 0.92720841 0.00000000 0.19543200 1.0