基础信息
化学式
La2ZnIrO6
MP-ID
mp-6152
元素数
4
位点数
20
密度
8.0827
g/cm³
体积
259.45
ų
晶胞参数 a
5.8229
Å
晶胞参数 b
5.5902
Å
晶胞参数 c
9.7279
Å
α 角
55.02
°
β 角
90.00
°
γ 角
90.00
°
空间群
P2_1/c
点群
2/m
晶体系统
Monoclinic
Bravais 格子
mP
稳定性
No
堆积分数
-
X 射线衍射
衍射图谱
横轴为 2θ (°)，纵轴为相对强度，Cu Kα ， λ=1.5418 Å
衍射峰（Top 24）
| 2θ | d (Å) | I | hkl |
|---|---|---|---|
| 18.87 | 4.7018 | 22.1 | (1,0,1) |
| 19.38 | 4.5803 | 5.8 | (0,1,0) |
| 19.41 | 4.5732 | 14.8 | (0,1,2) |
| 24.73 | 3.6000 | 7.7 | (1,1,0) |
| 24.75 | 3.5965 | 7.6 | (1,1,2) |
| 30.71 | 2.9114 | 44.1 | (2,0,0) |
| 31.54 | 2.8363 | 99.7 | (1,1,-1) |
| 31.58 | 2.8329 | 100.0 | (1,1,3) |
| 32.02 | 2.7951 | 49.5 | (0,2,2) |
| 32.75 | 2.7347 | 10.3 | (2,0,1) |
| 36.57 | 2.4571 | 4.8 | (2,1,0) |
| 36.59 | 2.4560 | 2.8 | (2,1,2) |
| 37.20 | 2.4171 | 3.5 | (1,0,3) |
| 37.41 | 2.4036 | 10.7 | (1,2,1) |
| 37.50 | 2.3981 | 3.7 | (0,1,4) |
| 40.64 | 2.2198 | 3.1 | (1,1,-2) |
| 40.69 | 2.2174 | 3.2 | (1,1,4) |
| 44.96 | 2.0163 | 41.9 | (2,2,2) |
| 45.52 | 1.9926 | 26.5 | (0,0,4) |
| 46.26 | 1.9625 | 6.1 | (2,0,3) |
| 46.44 | 1.9553 | 5.2 | (2,2,1) |
| 46.47 | 1.9542 | 5.2 | (2,2,3) |
| 48.26 | 1.8858 | 1.8 | (3,0,1) |
| 49.19 | 1.8524 | 3.3 | (2,1,-2) |
能量属性
形成能/原子
-2.65377
eV/atom
能量/原子
-7.61957
eV/atom
凸包距离
0.0301
eV/atom
未修正能量
-7.2074
eV/atom
体积/原子
12.97
ų
c/a 比
1.6706
电子属性
金属性
金属
带隙
0
eV
直接带隙
No
CBM
N/A
eV
磁性属性
磁性
Yes
总磁矩
2.0002
μB
磁有序
FM
磁性位点数
2
磁化强度/体积
0.007710
μB/ų
弹性属性
KVRH
151.657
GPa
GVRH
41.096
GPa
杨氏模量 E
113.074
GPa
泊松比 ν
0.376
Pugh 比 K/G
3.690
维氏硬度估算
-
GPa
韧性
Brittle
各向异性
0.517
拉梅 λ
124.260
GPa
特征分析
元素组成（原子分数）
组成信息
主元 / 基质元素
O · 0.600
元素家族
Metalloid-Nonmetal
溶质分数
0.400
间隙分数
0.000
综合指标雷达（归一化）
元素类别占比
混合熵 ΔS/R
1.0889
高熵判据（>1.0 视为高熵）
混合熵 ΔS
9.0531
J/mol·K
Ω 参数
1.0030
Ω > 1.1 利于固溶体形成
原子尺寸错配 δr
53.754%
δr < 6.6% 利于单相固溶
电负性差 Δχ
0.9873
越小混合越稳定
VEC
5.100
价电子浓度，影响相稳定性
混合焓 ΔH_mix
-5.548
kJ/mol 且负值为放热混合
熵归一化
0.7855
固溶体倾向
0
相趋势
IM
关联任务
引用参考
Materials Project 官方页面
https://materialsproject.org/materials/mp-6152
参考引用
The crystal structure and related material properties of La2ZnIrO6 were obtained from the Materials Project database (MP-ID: mp-6152, database version v2026.04.13).
文献引用
Horton, M.K., Huck, P., Yang, R.X. et al. Accelerated data-driven materials science with the Materials Project. Nat. Mater. 24, 1522–1532 (2025). https://doi.org/10.1038/s41563-025-02272-0
晶体结构 3D 渲染
加载 3D 结构...
样式: Ball & Stick
|
拖拽旋转 · 滚轮缩放 · 右键平移
原始 CIF 数据
# generated using pymatgen
data_La2ZnIrO6
_symmetry_space_group_name_H-M 'P 1'
_cell_length_a 5.82285400
_cell_length_b 5.59016200
_cell_length_c 9.72790091
_cell_angle_alpha 55.01963928
_cell_angle_beta 90.00000000
_cell_angle_gamma 90.00000000
_symmetry_Int_Tables_number 1
_chemical_formula_structural La2ZnIrO6
_chemical_formula_sum 'La4 Zn2 Ir2 O12'
_cell_volume 259.44669886
_cell_formula_units_Z 2
loop_
_symmetry_equiv_pos_site_id
_symmetry_equiv_pos_as_xyz
1 'x, y, z'
loop_
_atom_site_type_symbol
_atom_site_label
_atom_site_symmetry_multiplicity
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
La La0 1 0.55951800 0.73402500 0.75102300 1.0
La La1 1 0.05951800 0.26597500 0.74897700 1.0
La La2 1 0.94048200 0.73402500 0.25102300 1.0
La La3 1 0.44048200 0.26597500 0.24897700 1.0
Zn Zn4 1 0.50000000 0.50000000 0.50000000 1.0
Zn Zn5 1 0.00000000 0.50000000 0.00000000 1.0
Ir Ir6 1 0.50000000 0.00000000 0.00000000 1.0
Ir Ir7 1 0.00000000 0.00000000 0.50000000 1.0
O O8 1 0.52806800 0.84929300 0.24652200 1.0
O O9 1 0.02806800 0.15070700 0.25347800 1.0
O O10 1 0.47193200 0.15070700 0.75347800 1.0
O O11 1 0.97193200 0.84929300 0.74652200 1.0
O O12 1 0.80218000 0.65279600 0.55019600 1.0
O O13 1 0.30218000 0.34720400 0.94980400 1.0
O O14 1 0.19782000 0.34720400 0.44980400 1.0
O O15 1 0.69782000 0.65279600 0.05019600 1.0
O O16 1 0.20891200 0.75793900 0.05187900 1.0
O O17 1 0.70891200 0.24206100 0.44812100 1.0
O O18 1 0.79108800 0.24206100 0.94812100 1.0
O O19 1 0.29108800 0.75793900 0.55187900 1.0