基础信息
化学式
Cr2CoSe4
MP-ID
mp-686354
元素数
3
位点数
56
密度
5.7147
g/cm³
体积
1,112.93
ų
晶胞参数 a
4.8519
Å
晶胞参数 b
5.5876
Å
晶胞参数 c
49.3888
Å
α 角
121.09
°
β 角
103.84
°
γ 角
84.29
°
空间群
P1
点群
1
晶体系统
Triclinic
Bravais 格子
aP
稳定性
No
堆积分数
-
X 射线衍射
衍射图谱
横轴为 2θ (°)，纵轴为相对强度，Cu Kα ， λ=1.5418 Å
衍射峰（Top 24）
| 2θ | d (Å) | I | hkl |
|---|---|---|---|
| 2.14 | 41.2561 | 3.2 | (0,0,1) |
| 4.28 | 20.6280 | 3.4 | (0,0,2) |
| 6.43 | 13.7520 | 4.8 | (0,0,3) |
| 8.57 | 10.3140 | 2.0 | (0,0,4) |
| 12.87 | 6.8760 | 1.6 | (0,0,6) |
| 15.03 | 5.8937 | 4.7 | (0,0,7) |
| 16.76 | 5.2907 | 1.4 | (0,1,-2) |
| 17.19 | 5.1570 | 10.2 | (0,0,8) |
| 17.54 | 5.0554 | 9.9 | (0,1,-1) |
| 17.73 | 5.0014 | 2.0 | (0,1,-8) |
| 18.38 | 4.8277 | 1.7 | (1,0,-2) |
| 18.55 | 4.7832 | 24.5 | (0,1,0) |
| 18.91 | 4.6923 | 1.3 | (1,0,-4) |
| 19.36 | 4.5840 | 4.1 | (0,0,9) |
| 19.54 | 4.5437 | 1.9 | (1,0,-5) |
| 19.74 | 4.4964 | 5.1 | (0,1,1) |
| 21.40 | 4.1523 | 2.9 | (1,0,-7) |
| 22.59 | 3.9362 | 3.8 | (1,0,-8) |
| 23.21 | 3.8319 | 1.8 | (1,1,-7) |
| 23.35 | 3.8104 | 3.0 | (1,1,-5) |
| 23.45 | 3.7937 | 1.9 | (1,1,-8) |
| 23.71 | 3.7523 | 16.3 | (1,1,-4) |
| 23.73 | 3.7496 | 1.2 | (1,0,5) |
| 23.92 | 3.7200 | 1.4 | (1,0,-9) |
能量属性
形成能/原子
-0.40478
eV/atom
能量/原子
-6.17951
eV/atom
凸包距离
0.3182
eV/atom
未修正能量
-5.9098
eV/atom
体积/原子
19.87
ų
c/a 比
10.1792
电子属性
金属性
金属
带隙
0
eV
直接带隙
No
CBM
N/A
eV
磁性属性
磁性
Yes
总磁矩
41.7185
μB
磁有序
FiM
磁性位点数
26
磁化强度/体积
0.037490
μB/ų
弹性属性
弹性数据暂不开放
特征分析
元素组成（原子分数）
组成信息
主元 / 基质元素
Se · 0.571
元素家族
Metalloid-Nonmetal
溶质分数
0.429
间隙分数
0.000
综合指标雷达（归一化）
元素类别占比
混合熵 ΔS/R
0.9557
高熵判据（>1.0 视为高熵）
混合熵 ΔS
7.9457
J/mol·K
Ω 参数
14.0857
Ω > 1.1 利于固溶体形成
原子尺寸错配 δr
5.003%
δr < 6.6% 利于单相固溶
电负性差 Δχ
0.4098
越小混合越稳定
VEC
5.286
价电子浓度，影响相稳定性
混合焓 ΔH_mix
-0.653
kJ/mol 且负值为放热混合
熵归一化
0.8699
固溶体倾向
1
相趋势
SS
关联任务
关联的计算任务 ID（1 个）
引用参考
Materials Project 官方页面
https://materialsproject.org/materials/mp-686354
参考引用
The crystal structure and related material properties of Cr2CoSe4 were obtained from the Materials Project database (MP-ID: mp-686354, database version v2026.04.13).
文献引用
Horton, M.K., Huck, P., Yang, R.X. et al. Accelerated data-driven materials science with the Materials Project. Nat. Mater. 24, 1522–1532 (2025). https://doi.org/10.1038/s41563-025-02272-0
晶体结构 3D 渲染
加载 3D 结构...
样式: Ball & Stick
|
拖拽旋转 · 滚轮缩放 · 右键平移
原始 CIF 数据
# generated using pymatgen
data_Cr2CoSe4
_symmetry_space_group_name_H-M 'P 1'
_cell_length_a 4.85192508
_cell_length_b 5.58760914
_cell_length_c 49.38875093
_cell_angle_alpha 121.08558738
_cell_angle_beta 103.83926851
_cell_angle_gamma 84.29036171
_symmetry_Int_Tables_number 1
_chemical_formula_structural Cr2CoSe4
_chemical_formula_sum 'Cr16 Co8 Se32'
_cell_volume 1112.93076023
_cell_formula_units_Z 8
loop_
_symmetry_equiv_pos_site_id
_symmetry_equiv_pos_as_xyz
1 'x, y, z'
loop_
_atom_site_type_symbol
_atom_site_label
_atom_site_symmetry_multiplicity
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_occupancy
Cr Cr0 1 0.27479857 0.29920558 0.94268519 1.0
Cr Cr1 1 0.25641569 0.29085191 0.85521764 1.0
Cr Cr2 1 0.67125192 0.79107766 0.93467359 1.0
Cr Cr3 1 0.36042315 0.11256106 0.72354326 1.0
Cr Cr4 1 0.63745582 0.76108345 0.77289191 1.0
Cr Cr5 1 0.34579761 0.20716426 0.60161270 1.0
Cr Cr6 1 0.62538578 0.88449109 0.65159885 1.0
Cr Cr7 1 0.36521135 0.13026187 0.47249444 1.0
Cr Cr8 1 0.62904789 0.83180474 0.52351540 1.0
Cr Cr9 1 0.36050332 0.23622393 0.35293396 1.0
Cr Cr10 1 0.63943947 0.87559171 0.40092084 1.0
Cr Cr11 1 0.24215603 0.22137314 0.18368331 1.0
Cr Cr12 1 0.74440702 0.70883290 0.26982560 1.0
Cr Cr13 1 0.18653297 0.26044175 0.02123347 1.0
Cr Cr14 1 0.68718426 0.72852229 0.18201707 1.0
Cr Cr15 1 0.81788504 0.73481126 0.10297137 1.0
Co Co16 1 0.96231359 0.97033282 0.87436650 1.0
Co Co17 1 0.95480754 0.00481334 0.74976866 1.0
Co Co18 1 0.03297306 0.00940980 0.62648502 1.0
Co Co19 1 0.02259084 0.00854130 0.50140932 1.0
Co Co20 1 0.04239172 -0.01452937 0.37498012 1.0
Co Co21 1 0.04316412 0.03596364 0.25138720 1.0
Co Co22 1 0.37705409 0.29250548 0.10652661 1.0
Co Co23 1 0.69352093 0.71659526 0.02163022 1.0
Se Se24 1 0.09826212 0.77075454 0.90713405 1.0
Se Se25 1 0.43520150 0.82010877 0.97897006 1.0
Se Se26 1 0.15786024 0.89141144 0.78938530 1.0
Se Se27 1 0.58801390 0.26720876 0.90306195 1.0
Se Se28 1 0.25430460 0.65746791 0.84268289 1.0
Se Se29 1 0.15844931 0.81458704 0.66044934 1.0
Se Se30 1 0.19574544 0.88301071 0.03774123 1.0
Se Se31 1 0.64148189 0.32777546 0.77956151 1.0
Se Se32 1 0.29207182 0.67079207 0.72175644 1.0
Se Se33 1 0.17127418 0.84122342 0.53760127 1.0
Se Se34 1 0.75109804 0.12316842 0.83838682 1.0
Se Se35 1 0.69054827 0.33002173 0.65405728 1.0
Se Se36 1 0.33606210 0.67307313 0.59633789 1.0
Se Se37 1 0.16891261 0.78901274 0.40839822 1.0
Se Se38 1 0.83066621 0.20350805 0.71638423 1.0
Se Se39 1 0.67067187 0.31719993 0.52807592 1.0
Se Se40 1 0.31319774 0.65678215 0.46975331 1.0
Se Se41 1 0.25266058 0.87868557 0.28738935 1.0
Se Se42 1 0.81726019 0.14485714 0.58835270 1.0
Se Se43 1 0.71105342 0.32063019 0.40349789 1.0
Se Se44 1 0.35337262 0.66377709 0.34520477 1.0
Se Se45 1 0.78546767 0.08542510 0.08360571 1.0
Se Se46 1 0.83889721 0.17510262 0.46438447 1.0
Se Se47 1 0.75079626 0.34675225 0.28314792 1.0
Se Se48 1 0.40924100 0.73501846 0.22246968 1.0
Se Se49 1 0.88536746 0.29549424 0.97332471 1.0
Se Se50 1 0.84055274 0.10534070 0.33600620 1.0
Se Se51 1 0.29532275 0.58681033 0.08505477 1.0
Se Se52 1 0.60273983 0.19236613 0.14871825 1.0
Se Se53 1 0.89628377 0.24013924 0.21927060 1.0
Se Se54 1 0.71802760 0.40619339 0.04039207 1.0
Se Se55 1 0.11642325 0.68837039 0.15107090 1.0